Microstuctral studio frigus-mounted az31 magnesium Alloy via praecisione Polising- Trojan (Suzhou) material technology Co., Ltd.

Microstuctral studio frigus-mounted az31 magnesium Alloy via praecisione Polising

20-05-2025

AZ31 Magnesii Alloy est typical deformis magnesii mixturae. Cum magnesii sicut matricem, quod praebet mixturam cum basic propria humilis densitate, quae dat az31 magnesium stillix a significant utilitatem in lumine applications. Et eius princeps ductility, princeps scelerisque conductivity et bonum electro tutum possessionem, id est late in structural components de aerospace, automotive partes, electronic products et aliis agris.

Nunc, tenuis laminas az magnesium mixturae (AL%: 2.5-3.5, ZN%: 0.6-1.4, MN% 0,2-1.0 et Reliqua MG) sunt polita et sampled.

Et sample est interficiam in parvis pieces et directe embedded cum TJ2227 PROLIXUS Epoxy resinae et thetamount pressura frigus adscendens machina ad subsequent sem observationis. Deinde, in sample paratus in alpha208 Dual-control dual-pervideo molere et politicas apparatus. Quod specifica gradus sunt, ut sequitur:

I. Nam superficies stridor cum Silicon carbide sandpaper p800 / P1200 / P2000, ut ne adscendens, cera debet applicari ad superficiem Sandpaper. Tere cum parva vis valorem et intus stupam cum Vocatus post se.
II. Polising Polising per usura ys pannis et aqua-libero III-micronemonium poloning suspensionis.
III. Denique Polishing est peragitur per usura et poliendo panno et aqua, libero I-micron Alumina Polising Suspensio.

Metallographic Metallographic mn8 microscopium, superficies politum sample erat lenis et vox directionem erat evidenter visibilis. Nigrum granuloso tempus erat dura confortans tempus. In specifica compositionem tamen indiget ut resolvitur ab subsequent sem eds.